Factory Wholesale AISI 304 DIN 1.4306 JIS SUS304L GB 022Cr19Ni10 Stainless Steel
1: JIS SUS304L steel introduction
SUS304L has all the features of SUS304. Excellent corrosion resistance and heat resistance, good corrosion resistance, deep drawing and polishing properties can be maintained after welding or stress relieving.
2: JIS SUS304L Steel equivalent
| Country | Japan | Germany | USA | China |
| Standard | JIS | DIN(W-Nr.) | ASTM | GB/T |
| Grade | SUS304L | 1.4306 | 304 | 022Cr19Ni10 |
3: JIS SUS304L steel chemical composition
| Grade | C≤ | Si≤ | Mn | P≤ | S≤ | Cr | Mo | Ni | N≤ |
| 304 | 0.07 | 1.00 | 2.00 | 0.045 | 0.015 | 17.5-19.5 | / | 8.00-10.5 | 0.1 |
| 1.4306 | 0.30 | 1.00 | 2.00 | 0.045 | 0.03 | 18.0-20.0 | / | 8.00-12.0 | / |
| SUS304L | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 18.0-20.0 | / | 9.00-13.0 | / |
| 022Cr19Ni10 | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 18.0-20.0 | / | 8.00-12.0 | / |
4: JIS SUS304L steel mechanical properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as annealed, Solid Solution. If you want to know the properties, kindly contact the salesman.
5: JIS SUS304L steel overviews
| Size | Round | Dia 0.1-500mm |
| Plate/Flat/Block | Thickness 0.3mm-200mm | |
| Width 1mm-2500mm | ||
| Heat treatment | Annealed ; Solid Solution | |
| Surface condition | Black; Peeled; Polished; Machined;Sand blast etc | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
| Application | SUS304L is used in chemical, coal and petroleum environment with high resistance to intergranular corrosion; outdoor decoration materials, heat resistant parts and parts with difficulty in heat treatment. Refrigerated and exterior materials, automotive exhaust pipes and heat-resistant equipment components. | |
6: Delivery condition
For hot forged bar, usually the delivery condition is hot forged, annealed/solid solution, rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed/solid solution, Black surface.
For hot rolled plate, usually the delivery condition is hot rolled, annealed/solid solution, black surface.
For cold drawn bar, usually the delivery condition is cold drawn, annealed/QT, peeled/black surface
We are professional manufacturer for many years. we can provide a wide range of steel products.
Usually bundling for large diameter,small diameter bars in bulk or as customer's demand.
The hardness after heat treatment is higher than D2/1.2379/Cr12Mo1V1, and can reach 61-63HRC after high-temperature tempering (525 ± 5 ℃); In terms of strength and wear resistance, it exceeds Cr12Mo1V1, and its toughness is higher than D2/1.2379/Cr12Mo1V1; The manufactured molds rarely have cracks and fissures, greatly improving their service life; The residual stress after wire cutting processing is smaller than that of Cr12Mo1V1; The cutting and grinding performance exceeds Cr12Mo1V1.
Suitable for manufacturing precision punching dies and stamping dies for cold forging, deep drawing, and wire rolling for wire cutting processing.