Manufacturer Direct DIN 1.2601 Cold Drawn Alloy Structural Steel Round Bar
1: DIN 1.2601 steel introduction
DIN 1.2601 is a Cold work tool alloy steel material grade.it is shock resisting steel. Digital Grade material number 1.2601 use in extrusion moulds, Hot Cast moulds. like aluminium production, Aluminium cutting mold. Our Tool Steel material 100 % ultrasonic tested with good price. Small size steel products make by hot rolled, large size steel products make by forging. 1.2601 with is equivalent Belong to DIN.
2: DIN 1.2601 steel equivalent
| Country | China | Japan | Germany | USA | UK |
| Standard | GB/T 1299 | JIS G4404 | DIN EN ISO4957 | ASTM A681 | BS 4659 |
| Grade | Cr12MoV | 1.2601 | D5 |
3: DIN 1.2601 steel chemical composition
| Grade | C | Mn | P | S | Si | W | V | Cr | ||||||
| DIN 1.2601 | 1.55 | 1.75 | 0.20 | 0.40 | 0.03 | 0.03 | 0.25 | 0.40 | 0.40 | 0.6. | 0.1 | 0.50 | 11.0 | 12.0 |
4: DIN 1.2601 steel mechanical properties
| Grade | Tensile strength | Yield strength | Elongation | Reduction | Impact Value | Hardness |
| DIN 1.2601 | 488 (≥)MPa | 12% | 31% | 31J | Annealing 225 HB max, Q+T: 58-63 HRc |
5: DIN 1.2601 steel overviews
| Size | Round | Dia 6-1200mm | |
| Plate/Flat/Block | Thickness 6mm-500mm | ||
| Width 20mm-1000mm | |||
| Process | EAF+LF+VD+Forged+Heat treatment(optional) | ||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | ||
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | ||
| Delivery condition | Forged; Hot rolled; Cold drawn | ||
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | ||
| Payment terms | T/T;L/C;/Money gram/ Paypal | ||
| Trade terms | FOB; CIF; C&F; etc.. | ||
| Packing | Standard Packages, or as Customers Request | ||
| Delivery time | 30-45 days | ||
| Application | DIN 1.2601 is suitable for applications High alloyed CrMoV steel for cutting tool and cold work tool steel. | ||
6:Heat treatment
Annealing:
Temperature/℃: 800~830; After the annealing, degree of hardness ≤HBS: 255
Quenching:
Hardening temperature/℃: 980~1010, Quenching in oil or air
Tempering:
Commonly used drawing temperature/℃: 180~250; After tempering hardness HRC | 100 ℃ : 63; After tempering hardness HRC | 200 ℃ : 61; After tempering hardness HRC | 300 ℃ : 60 ; After tempering hardness HRC | 400 ℃ : 58
Normalizing
at Normalizing temperature, then cool in furnace
7: Delivery condition
For hot forged or hot rolled bar, usually the delivery condition is hot forged or rolled, annealed, rough turned.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface.
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface
We are professional manufacturer for many years. we can provide a wide range of steel products.
Usually bundling for large diameter,small diameter bars in bulk or as customer's demand.
The hardness after heat treatment is higher than D2/1.2379/Cr12Mo1V1, and can reach 61-63HRC after high-temperature tempering (525 ± 5 ℃); In terms of strength and wear resistance, it exceeds Cr12Mo1V1, and its toughness is higher than D2/1.2379/Cr12Mo1V1; The manufactured molds rarely have cracks and fissures, greatly improving their service life; The residual stress after wire cutting processing is smaller than that of Cr12Mo1V1; The cutting and grinding performance exceeds Cr12Mo1V1.
Suitable for manufacturing precision punching dies and stamping dies for cold forging, deep drawing, and wire rolling for wire cutting processing.