Manufacturer Direct Sales DIN 1.0718 Hot Forged Annealed Steel Round Bar
1: DIN 1.0718 steel introduction
12L14 is easy cutting structural steel, easy cutting steel is easy to be (turning, milling, drawing, planing, drilling, etc.) cutting processing steel, also known as automatic machine tool processing steel, referred to as automatic steel. It is produced to adapt to machining automation and flow line production.
2: DIN 1.0718 steel equivalent
| Country | China | Japan | Germany | USA | UK |
| Standard | GB | JIS | DIN (W-Nr.) EN 10277 | AISI/ASTM | BS 970-3-1991 |
| Grade | SUM24L | 1.0718 | 12L14 |
3: DIN 1.0718 steel chemical composition
| Grade | C | Si | Mn | P | Pb |
| 1.0718 | 0.14 | 0.05 | 0.90-1.30 | 0.11 | 0.20-0.35 |
| 12L14 | 0.15 | 0.26-0.35 | 0.85-1.15 | 0.04-0.09 | 0.15-0.35 |
4: DIN 1.0718 steel mechanical properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
5: DIN 1.0718 steel overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block | Thickness 6mm-500mm | |
| Width 20mm-1000mm | ||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
| Application | 12L14 is mainly used for making instruments and meters, watch parts, automobiles, machine tools and other machines with small stress and strict requirements on size and finish. Standard parts with strict requirements for dimensional accuracy and smoothness and relatively low requirements for mechanical properties, such as gear, shaft, bolt, valve, bushing, pin, pipe joint, spring seat and machine tool lead screw, plastic molding die, surgical and dental appliances, etc. | |
7: Delivery condition
For hot forged bar, usually the delivery condition is hot forged, annealed/QT, rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed/QT, Black surface.
For hot forged block, usually the delivery condition is hot forged, annealed/QT, milled surface/Black surface
For hot rolled plate, usually the delivery condition is hot rolled, annealed/QT, black surface.
For cold drawn bar, usually the delivery condition is cold drawn, annealed/QT, peeled/black surface
We are professional manufacturer for many years. we can provide a wide range of steel products.
Usually bundling for large diameter,small diameter bars in bulk or as customer's demand.
The hardness after heat treatment is higher than D2/1.2379/Cr12Mo1V1, and can reach 61-63HRC after high-temperature tempering (525 ± 5 ℃); In terms of strength and wear resistance, it exceeds Cr12Mo1V1, and its toughness is higher than D2/1.2379/Cr12Mo1V1; The manufactured molds rarely have cracks and fissures, greatly improving their service life; The residual stress after wire cutting processing is smaller than that of Cr12Mo1V1; The cutting and grinding performance exceeds Cr12Mo1V1.
Suitable for manufacturing precision punching dies and stamping dies for cold forging, deep drawing, and wire rolling for wire cutting processing.